Attribute Name
|
Value
|
---|---|
Abrasive Material
|
Cerium Oxide
|
Application
|
Finishing, Sanding
|
Attachment Type
|
PSA
|
Backing Material
|
Film
|
Backing Thickness (Imperial)
|
3 mil
|
Brand
|
Trizact™
|
Coat Type
|
Closed Coat
|
Color Family
|
White
|
Equipment - Machines
|
Random Orbital Sanders
|
Hole Configuration
|
500X
|
Industries
|
Composite, Marine, Woodworking
|
Maximum Speed
|
12000 rpm
|
Overall Diameter (Imperial)
|
5 in
|
Overall Diameter (Metric)
|
127 mm
|
Product Color
|
White
|
Product Form
|
Disc Roll
|
Substrate
|
Composite, Paint
|
TDS Required
|
No
|
3M™ Trizact™ PSA Film Disc Roll 568XA utilizes microreplicated cerium oxide uniformly distributed across a 3-mil film backing to create a high gloss on glass, and solid surfaces. Use 568XA film discs wet. Pressure sensitive adhesive backing in disc roll form makes handling and attachment easy.
Trizact Abrasives
3M™ Trizact™ abrasives are engineered using 3M microreplication — the creation of microscopic 3-dimensional structures applied to a backing in a uniform and precise pattern. These pyramid-like structures contain multiple layers of mineral. When they break down during use, fresh cutting mineral continues to be exposed so results are consistent throughout the life of the abrasive.
Ongoing sharp cutting action contributes to higher throughput, more uniform results and greater productivity.
Polishes and Leaves Glass Crystal Clear
Use 3M™ Trizact™ 568XA discs for a final polish. First, wet the surface slightly with a small amount of water. As you polish, the mineral "pyramids" will break down to form a slurry-like solution. The polishing action that occurs will remove scratches left by previous leveling steps.
For acrylic-filled solid surfaces, use 568XA damp as a final step to attain a high-gloss finish.
Remove silica coatings (anti-glare and static) and fluoric acid spots in a single step with 568XA.