Attribute Name
|
Value
|
---|---|
Adhesion Strength
|
480 oz/in
|
Adhesive Type
|
Acrylic
|
Alternative Sale Availability
|
6. This item is for industrial use only and there are no VOC restrictions.
|
Application
|
Bonding Composite Materials
|
Brand
|
Scotch-Weld™
|
Color Family
|
Black
|
Container Size (Imperial)
|
5.28 Gallon
|
Container Size (Metric)
|
20 Liter
|
Full Cure Time
|
8-24 Hours @ 72 F (22 C)
|
Industries
|
Construction, Consumer Goods, Electronics, General Industrial, Metalworking, Military & Government, Specialty Vehicle, Transportation
|
Mix Ratio Volume Base:Accelerator
|
1 : 1
|
Open Time
|
10 min @ 72 °F (22 °C)
|
Physical Form
|
Flowable Liquid
|
Product Color
|
Black
|
Product Form
|
Liter
|
Product Type
|
Acrylic
|
Set Time
|
10 min
|
Shear Strength
|
3600 psi
|
Shelf Life in Months (From Date of Manufacture)
|
12
|
Specific Gravity
|
1.07
|
Storage Temperature
|
<=40 Degree Fahrenheit
|
Storage Temperature (Celsius)
|
4 °C
|
Substrate
|
Ceramic, Glass, Hardwood, Metal, Plastic (ABS, PVC, Acrylic), Plastic (High Performance Nylon), Wood
|
Substrate 1
|
Epoxy - Fiber Reinforced, Glass & Ceramics, Metal, Nylon - Fiber Reinforced, Plastic (ABS, PVC, Acrylic), Plastic (High Performance Nylon), Wood & Hardboard
|
Substrate 2
|
Epoxy - Fiber Reinforced, Glass & Ceramics, Metal, Nylon - Fiber Reinforced, Plastic (ABS, PVC, Acrylic), Plastic (High Performance Nylon), Wood & Hardboard
|
Units per Case
|
1
|
Viscosity
|
Self-leveling
|
Viscosity Range (cps) at Room Temperature
|
17,000-21,000
|
Volatile Organic Compounds (VOCs)
|
See Safety Data Sheet, Regulatory Data Sheet
|
Volume (Metric)
|
20 L
|
3M™ Scotch-Weld™ Low Odor Acrylic Adhesive DP810 Black is a toughened two-part, room-temperature curing acrylic adhesive specially formulated to bond oily metals, plastics, and other surfaces. With lower odor and non-flammable properties, 3M™ Scotch-Weld™ Acrylic Adhesive DP810 Black contributes to a safer work environment compared to typical acrylic adhesives.
When using a Duo-Pak (DP) size adhesive, rely on 3M dispensing equipment for convenient and accurate metering, mixing and dispensing.
Provides High Shear and Peel Strength and is Toughened for Impact Resistance
This unique acrylic gives you the strong shear and peel strength along with good impact resistance for durability to meet demanding end-use applications. Making work safer, faster, and more efficient, that's just a few of the benefits of 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive DP810 Black. It bonds on a variety of substrates ranging from metals, composite and many plastics including nylon. The acrylic adhesive cures to a tan or black color.
Recommended Applications
10 Minute Work Life and 20 Minute Handling Strength
With a mix ratio is 1:1, 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive DP810 Black provides a 10 minute work life to allow time to adjust fit prior to setting. The adhesive reaches handling strength in approximately 20 minutes and is fully cured in 8-24 hours (at 72°F/22°C). (Note: excess adhesive exposed to air around the bond lines may remain tacky up to 48 hrs.) 3M™ Scotch-Weld™ Low Odor Acrylic Adhesive DP810 Black is approved under UL 746C, polymeric materials use in electrical equipment.
Easy Adhesion with Acrylic
Acrylic adhesives, often referred to as epoxy adhesives or epoxy glue, are two-part adhesives that provide excellent bond strength and durability, although slightly lower adhesion than 2 part epoxy in some situations. However, acrylic glues have several features that make them easier to use, including a much faster cure speed, higher tolerance for oily or unprepared bonding surfaces and the ability to bond a wide variety of materials, including nearly all plastics. Newer acrylic adhesive formulations are room temperature stable with a moderate shelf life.